SOGUT® Socketing Resin

Request Samples

Overview

Two-component cold-pour socketing resin for structural wire rope terminations in marine and civil infrastructure applications.

Designed for ambient-temperature installation as an alternative to molten alloy socket casting.

Mechanical Performance

Property	SI Value	US Value (approx.)	Test Method
Density	1.832 g/cm³	114.4 lb/ft³	GB/T 1033.1-2008
Tensile Strength	21.6 MPa	3.13 ksi	GB/T 2567
Tensile Modulus	10.7 GPa	1.55 Msi	GB/T 2567
Flexural Strength	60.0 MPa	8.70 ksi	GB/T 2567
Flexural Modulus	10.0 GPa	1.45 Msi	GB/T 2567
Compressive Strength	116.0 MPa	16.8 ksi	GB/T 2567-2021
Compressive Modulus	6.547 GPa	0.95 Msi	GB/T 2567-2021
Heat Deflection Temperature (HDT)	120 °C	248 °F	GB/T 1634.2-2019
Barcol Hardness	70	70	GB/T 3854-2017
Tensile Lap-Shear Strength	16.8 MPa	2.44 ksi	GB/T 7124

Representative laboratory results verified by a third-party testing laboratory under applicable GB/T standards (test report No. 2025-GC09016). Additional project-specific validation (including ASTM) can be coordinated upon request.

Performance values are typical laboratory results and are not design guarantees. Detailed test methodology and supporting documentation are available upon request.

Applications

Marine mooring systems
Bridge cable anchorage
Structural wire rope terminations
Heavy civil infrastructure

Engineering Advantages

Ambient-temperature installation; no molten alloy required.
Two-component formulation with defined mixing ratio.
Formulated for structural load transfer within socket terminations.
Laboratory test reports and technical documentation available upon request.

Installation Overview

Prepare socket and wire rope termination.
Confirm components within recommended temperature range.
Mix Component A and Component B at specified ratio.
Pour mixture into socket cavity ensuring full encapsulation.
Maintain alignment during initial cure period.

Socket Condition Images

Broomed steel wire rope strands prior to resin casting — Broomed wire rope strands prepared prior to cold-pour resin casting.

Fully cured socket condition showing encapsulated broomed steel strands within the socket cavity. — Fully cured resin encapsulating broomed steel strands within the socket cavity. Representative laboratory and field condition.

12 mm wire rope sling tensile test — typical break appearance — 12 mm wire rope sling tensile test — typical break appearance (verification photo).

Storage & Handling

Store sealed between 10-30°C in dry conditions.
Protect from moisture and direct sunlight.
Refer to SDS for handling and transport classification.

Packaging & Kit Sizes

SOGUT two-component socketing resin product packaging

Supplied as paired two-component kits. Project-scale packaging configurations available upon request.

Standard kit volumes:

• 500 mL
• 1,000 mL
• 2,000 mL
• 3,000 mL

Need qualification samples or technical documentation?

Request Samples Request Technical Documentation

Qualification sample kits available upon request.

Shipping coordinated under applicable dangerous goods regulations.

Downloads

SOGUT® Socketing Resin – Technical Data Sheet

Technical data sheet including product description, mechanical performance values, application scope, and handling guidance.

SOGUT® Socketing Resin – Safety Data Sheet (Component A)

GHS-compliant safety data sheet for the liquid resin component (UN1866, Class 3).

SOGUT® Socketing Resin – Safety Data Sheet (Component B)

GHS-compliant safety data sheet for the powder component.